Interaction between precipitation, normal grain growth, and secondary recrystallisation in austenitic stainless steel containing particles

Nenhuma Miniatura disponível
Citações na Scopus
11
Tipo de produção
Artigo
Data
1999
Autores
Padilha A.F.
Dutra J.C.
Randle V.
Orientador
Periódico
Materials Science and Technology
Título da Revista
ISSN da Revista
Título de Volume
Citação
PADILHA, A. F.; DUTRA, J. C.; RANDLE, Valerie. Interaction between precipitation, normal grain growth, and secondary recrystallisation in austenitic stainless steel containing particles. MATERIALS SCIENCE AND TECHNOLOGY, v. 15, n. 9, p. 1009-1014, 1999.
Texto completo (DOI)
Palavras-chave
Resumo
With the aid of various complementary methods of microstructural analysis, the precipitation, grain growth, and secondary recrystallisation behaviour of an 15Cr-15Ni-1.2Mo-Ti-B (wt-%) austenitic stainless steel were studied over prolonged periods of time in the temperature range 600-1300°C. The experimental results showed that several types of precipitates were present in the material, and that the dissolution temperatures of each of these correlated with the type and extent of grain growth which was observed. It was, therefore, concluded that in the present study secondary recrystallisation was caused directly by the interaction of precipitates with grain boundaries. Furthermore, secondary recrystallisation produced a strong, predominantly {122} 〈012〉 texture which has not previously been reported. © 1999 IoM Communications Ltd.