Influence of sigma phase formation on pitting corrosion of an aged uns s31803 duplex stainless steel

Página do item simplificado
dc.contributor.authorDos Santos D.C.
dc.contributor.authorMagnabosco R.
dc.contributor.authorDe Moura-Neto C.
dc.date.accessioned2019-08-20T00:17:37Z
dc.date.available2019-08-20T00:17:37Z
dc.date.issued2013
dc.description.abstractThe main purpose of this contribution was the study of the relation between sigma formation and pitting corrosion resistance of a UNS S31803 duplex stainless steel aged at 850°C. Solution-treated samples were isothermally aged at 850°C for up to 360 h. The corrosion resistance of aged UNS S31803 steel was analyzed through cyclic potentiodynamic polarization tests in 0.6 M sodium chloride (NaCl) solution. The main mechanism of sigma phase formation was nucleation and growth from ferrite, in agreement to the Johnson-Mehl-Avrami- Kolmogorov kinetics model. This model suggests a change on the mechanisms of sigma phase formation from nucleation and growth from ferrite to the growth from austenite. Pitting morphology was related to the material microstructure. The pitting growth mechanism occurred by selective corrosion of the chromium-depleted areas of the specimens. Both pitting and repassivation potentials decreased with an increase of sigma volume fraction. Recovery of the corrosion resistance was observed in the early stages of sigma formation, probably related to chromium redistribution to depleted areas. © 2013, NACE International.
dc.description.firstpage900
dc.description.issuenumber9
dc.description.lastpage911
dc.description.volume69
dc.identifier.citationDOS SANTOS, DANIELLA CALUSCIO; MAGNABOSCO, RODRIGO; DE MOURA-NETO, CARLOS. Influence of sigma phase formation on pitting corrosion of an aged UNS S31803 duplex stainless steel.. Corrosion (Houston, Tex.), v. 69, n. 9, p. 900-911, 2013.
dc.identifier.doi10.5006/0768
dc.identifier.issn0010-9312
dc.identifier.urihttps://repositorio.fei.edu.br/handle/FEI/2298
dc.relation.ispartofCorrosion
dc.rightsAcesso Restrito
dc.subject.otherlanguageDuplex stainless steel
dc.subject.otherlanguageJohnson-Mehl-avrami
dc.subject.otherlanguagePitting corrosion
dc.subject.otherlanguagePolarization
dc.subject.otherlanguageSigma
dc.titleInfluence of sigma phase formation on pitting corrosion of an aged uns s31803 duplex stainless steel
dc.typeArtigo
fei.scopus.citations31
fei.scopus.eid2-s2.0-84883622911
fei.scopus.subjectCyclic potentiodynamic polarization
fei.scopus.subjectDuplex stainless steel
fei.scopus.subjectJohnson-mehl-avrami
fei.scopus.subjectMaterial microstructures
fei.scopus.subjectNucleation and growth
fei.scopus.subjectRepassivation potential
fei.scopus.subjectSigma
fei.scopus.subjectSodium chloride solution
fei.scopus.updated2024-03-04
fei.scopus.urlhttps://www.scopus.com/inward/record.uri?partnerID=HzOxMe3b&scp=84883622911&origin=inward
Arquivos
Coleções
Artigos