Ferrite-to-austenite transformation during cold working of a duplex stainless steel
Nenhuma Miniatura disponível
Citações na Scopus
0
Tipo de produção
Artigo de evento
Data
2011-09-23
Autores
Rodrigo Magnabosco
TAVARES, D. B.
FORGAS, A.
DE MOURA NETO, C.
TAVARES, D. B.
FORGAS, A.
DE MOURA NETO, C.
Orientador
Periódico
7th European Stainless Steel Conference: Science and Market, Proceedings
Título da Revista
ISSN da Revista
Título de Volume
Citação
MAGNABOSCO, R.; TAVARES, D. B.; FORGAS, A.; DE MOURA NETO, C.
Ferrite-to-austenite transformation during cold working of a duplex stainless steel. 7th European Stainless Steel Conference: Science and Market, Proceedings, sept. 2011.
Texto completo (DOI)
Palavras-chave
Resumo
Ferrite-austenite duplex stainless steels (DSS) are replacing austenitic stainless steels in many applications due to its high mechanical and corrosion resistance. However, magnetic measurements of ferrite volume fraction using a ferritscope of cold worked samples indicate a reduction in the ferrite content with increasing mechanical work. Considering this fact, this work studies the influence of the cold working on the ferrite/austenite ratio. Samples of UNS S31803 DSS sheet, originally 3 mm thick, were solution-treated at 1175°C for 30 minutes and water quenched; after that, different levels of cold working were applied. Ferrite volume fraction was determined using two distinct methods: quantitative stereology with an optical microscope and magnetic measurements using a ferritscope; a detailed microstructural characterization, including X-ray diffractometry, was conducted to base the discussion of a possible ferrite-to-austenite diffusionless transformation.