Intermetallic phases formation during short aging between 850 °c and 950 °c of a superduplex stainless steel
Nenhuma Miniatura disponível
Citações na Scopus
15
Tipo de produção
Artigo
Data
2012
Autores
Magnabosco R.
Dos Santos D.C.
Dos Santos D.C.
Orientador
Periódico
Journal of Materials Research and Technology
Título da Revista
ISSN da Revista
Título de Volume
Citação
R. Magnabosco; D. C. dos Santos. Intermetallic Phases Formation During Short Aging between 850°C and 950°C of a Superduplex Stainless Steel. Journal of Materials Research and Technology, v. 1, n. 2, p. 71-74, 2012.
Texto completo (DOI)
Palavras-chave
Resumo
This paper is based on the study of intermetallic phase formation during aging between 850 C and 950 C, for periods up to 5 min; those treatments were conducted in liquid aluminum bath, allowing fast heating of the small sized specimens. It was found that backscattered electron images could be used in the automatized routines of quantitative stereology of intermetallic phases and nitrides found in duplex and superduplex stainless steels. A measurable intermetallic phase fraction was observed just after 1 min aging in the studied temperatures, but it was not possible to distinguish sigma and chi phases from the observed intermetallic phases. Nitrides were also observed, but they were probably formed in steel manufacturing, since there was no significant influence of aging on its volume fraction. © 2012 Elsevier Editora Ltda. and Brazilian Metallurgical, Materials and Mining Association.