Impacto nas Propriedades Mecânicas e Tensões Residuais do Material ASTM A572 Grau 50 Soldado por Arco Submerso com Alívio de Tensões Térmico
Carregando...
Arquivos
Citações na Scopus
1
Tipo de produção
Artigo
Data
2019-10-29
Autores
VIEIRA, FERNANDO DIAS
AL-RUBAIE, KASSIM SHAMIL FADHIL
PRETI, ORLANDO
RICHTER, RINGO OTTMAR
Sergio Delijaicov
AL-RUBAIE, KASSIM SHAMIL FADHIL
PRETI, ORLANDO
RICHTER, RINGO OTTMAR
Sergio Delijaicov
Orientador
Periódico
REVISTA SOLDAGEM E INSPEÇÃO
Título da Revista
ISSN da Revista
Título de Volume
Citação
VIEIRA, F. D.; AL-RUBAIE, K. S. F.; PRETI, O.; RICHTER, R. O.; DELIJAICOV, Sergio. Impacto nas propriedades mecânicas e tensões residuais do material ASTM A572 Grau 50 soldado por arco submerso com alívio de tensões térmico. REVISTA SOLDAGEM E INSPEÇÃO, v. 24, p. 1-10, 2019.
Texto completo (DOI)
Palavras-chave
Aerogeradores,Alívio de tensões térmico,Propriedades mecânicas,Solda arco submerso,Windgenerators,Post weld heat treatment,Mechanical properties,Submerged arc welding
Resumo
O aço ASTM A572 Grau 50 é utilizado na fabricação de conjuntos soldados para aerogeradores, por este motivo, a realização de alívio de tensões é de grande importância para correção dos impactos causados pelos processos de soldagem, bem como, o conhecimento das propriedades finais obtidas com a realização deste processo. O objetivo desse estudo é comparar as propriedades mecânicas e tensões residuais (método de furo cego) em amostras de aço ASTM A572 Grau 50, soldadas pelo processo de arco submerso, submetidas ao alívio de tensões na condição térmica (PWHT) e na condição como soldado (SST), seguindo os requisitos normativos da AWS D1.1-2015. Os resultados da condição PWHT referente a dureza, limite de escoamento, resistência a tração e tensões residuais são menores e os valores de alongamento e energia absorvida ao impacto são maiores do que a condição SST. Ambas as condições foram aprovadas no ensaio de dobramento lateral. Os resultados obtidos demonstram a importância do processo de alivio de tensões que minimiza os efeitos indesejados dos processos de soldagem aos componentes.
The ASTM A572 Grade 50 material is used in welded structural components in the manufacture of wind turbines. In this way, it is important to apply the stress relief process to correct the effects caused by the welding processes, and then assess the final properties obtained with this process. The objective of this article is to evaluate the mechanical properties of specimens of the ASTM A572 Grade 50 material welded by the submerged arc welding, comparing the thermal stress relief condition (PWHT) with the as welded condition (SST), following the normative requirements of AWS D1. 1-2015. Tensile testing, impact test, lateral bending, hardness and residual stresses measured by hole drilling method for the conditions tested. The results showed lower values of hardness, residual stress, yield strength, and ultimate tensile strength of the PWHT specimens. On the other hand, the values of elongation and impact energy absorbed of the PWHT specimens were higher than those of the SST specimens. Both conditions tested were approved in the lateral bending test. The results demonstrate the importance of the stress relief process, which reduces the unwanted effects of the welding processes, thereby delivering better quality of the components
The ASTM A572 Grade 50 material is used in welded structural components in the manufacture of wind turbines. In this way, it is important to apply the stress relief process to correct the effects caused by the welding processes, and then assess the final properties obtained with this process. The objective of this article is to evaluate the mechanical properties of specimens of the ASTM A572 Grade 50 material welded by the submerged arc welding, comparing the thermal stress relief condition (PWHT) with the as welded condition (SST), following the normative requirements of AWS D1. 1-2015. Tensile testing, impact test, lateral bending, hardness and residual stresses measured by hole drilling method for the conditions tested. The results showed lower values of hardness, residual stress, yield strength, and ultimate tensile strength of the PWHT specimens. On the other hand, the values of elongation and impact energy absorbed of the PWHT specimens were higher than those of the SST specimens. Both conditions tested were approved in the lateral bending test. The results demonstrate the importance of the stress relief process, which reduces the unwanted effects of the welding processes, thereby delivering better quality of the components