Selective corrosion of 550°C aged Cu10Ni-3Al-1.3Fe alloy in NaCl aqueous solution
Nenhuma Miniatura disponível
Citações na Scopus
9
Tipo de produção
Artigo
Data
2011
Autores
Liberto R.C.N.
Magnabosco R.
Alonso-Falleiros N.
Magnabosco R.
Alonso-Falleiros N.
Orientador
Periódico
Corrosion Science
Título da Revista
ISSN da Revista
Título de Volume
Citação
Liberto, Rodrigo César Nascimento; Magnabosco, Rodrigo; ALONSO-FALLEIROS, Neusa. Selective corrosion of 550°C aged Cu10Ni 3Al 1.3Fe alloy in NaCl aqueous solution. Corrosion Science, n. 5, p. 1976-1982, 2011.
Texto completo (DOI)
Palavras-chave
Resumo
This work studied the electrochemical behavior of a solution treated or 550°C aged Cu10Ni-3Al-1.3Fe alloy, in 0.01M NaCl aqueous solution, through potentiodynamic polarization in both stagnant condition or under erosion process. Results showed the occurrence of a passivity break potential (Epb), related to the beginning of the denickelification process, which occurred as a localized attack under stagnant electrolyte. Under erosion conditions localized denickelification was not observed, despite of the presence of Epb. This could indicate that selective corrosion of Ni, which caused the observed Epb, occurred as a dissolution-redeposition process, with removal of the Cu deposits during erosion process. © 2011 Elsevier Ltd.