Selective corrosion of 550°C aged Cu10Ni-3Al-1.3Fe alloy in NaCl aqueous solution

Página do item simplificado
dc.contributor.authorLiberto R.C.N.
dc.contributor.authorMagnabosco R.
dc.contributor.authorAlonso-Falleiros N.
dc.date.accessioned2019-08-20T00:17:36Z
dc.date.available2019-08-20T00:17:36Z
dc.date.issued2011
dc.description.abstractThis work studied the electrochemical behavior of a solution treated or 550°C aged Cu10Ni-3Al-1.3Fe alloy, in 0.01M NaCl aqueous solution, through potentiodynamic polarization in both stagnant condition or under erosion process. Results showed the occurrence of a passivity break potential (Epb), related to the beginning of the denickelification process, which occurred as a localized attack under stagnant electrolyte. Under erosion conditions localized denickelification was not observed, despite of the presence of Epb. This could indicate that selective corrosion of Ni, which caused the observed Epb, occurred as a dissolution-redeposition process, with removal of the Cu deposits during erosion process. © 2011 Elsevier Ltd.
dc.description.firstpage1976
dc.description.issuenumber5
dc.description.lastpage1982
dc.description.volume53
dc.identifier.citationLiberto, Rodrigo César Nascimento; Magnabosco, Rodrigo; ALONSO-FALLEIROS, Neusa. Selective corrosion of 550°C aged Cu10Ni 3Al 1.3Fe alloy in NaCl aqueous solution. Corrosion Science, n. 5, p. 1976-1982, 2011.
dc.identifier.doi10.1016/j.corsci.2011.02.018
dc.identifier.issn0010-938X
dc.identifier.urihttps://repositorio.fei.edu.br/handle/FEI/2275
dc.relation.ispartofCorrosion Science
dc.rightsAcesso Restrito
dc.subject.otherlanguageA. Alloy
dc.subject.otherlanguageA. Copper
dc.subject.otherlanguageB. Polarization
dc.subject.otherlanguageC. Pitting corrosion
dc.titleSelective corrosion of 550°C aged Cu10Ni-3Al-1.3Fe alloy in NaCl aqueous solution
dc.typeArtigo
fei.scopus.citations9
fei.scopus.eid2-s2.0-79952899497
fei.scopus.subjectA. Alloy
fei.scopus.subjectA. Copper
fei.scopus.subjectB. Polarization
fei.scopus.subjectC. Pitting corrosion
fei.scopus.subjectDenickelification
fei.scopus.subjectElectrochemical behaviors
fei.scopus.subjectErosion conditions
fei.scopus.subjectErosion process
fei.scopus.subjectNaCl aqueous solution
fei.scopus.subjectRedeposition
fei.scopus.subjectSelective corrosion
fei.scopus.updated2024-11-01
fei.scopus.urlhttps://www.scopus.com/inward/record.uri?partnerID=HzOxMe3b&scp=79952899497&origin=inward
Arquivos
Coleções
Artigos